Hysol ® 9460F
You may print this page for your file
Epoxy Adhesive 

Description
Hysol 9460F is a faster cure version of 9460. The handling strength and pot life are reduced by approximately 50% while maintaining most of the performance of Hysol 9460.

Recommend Substrates: metals, phenolic plastics, polyester, hard boards and forestry products, ceramics rubber, masonry materials and other construction materials.
 
Features
Shortened Pot Life                       Fast Handling                                  StrengthGood Peel Strength
Non-Sag /Slump Resistant        Good Tensile Sheer Strength          Easily Mixed/Easily Dispensed

Typical Properties
                                                                                              Part A                Part B                   Mixed
Color                                                                                     White                 Black                    Grey
Viscosity, Poise                                                                     1500-3000          1000-2500            1500-2500
Shelf Life @ 90°F,                                                                 1 year                 1 year                    --

Handling
Mixing: This product requires mixing two components together just prior to the application. Complete mixing is necessary. The temperature of the separate components prior to mixing is not critical, but they should be at room temperature.
                                                                                               Part A                            Part B
By weight                                                                               100                                  100
By volume                                                                              1                                      1
Pot life @  RT 250 grams                                                     15-20 minutes

Application
Mixing – Bulk: Combine Part A (resin) and Part B (hardener) in the correct ratio and mix thoroughly. Continue to mix until all white and black streaks are gone and mix is uniformly grey. This is important! Heat build-up during or after mixing is normal. Do not mix quantities greater than two pounds as dangerous heat build-up can occur causing uncontrolled decomposition of the mixed adhesive. Mixing smaller quantities will minimize the heat build-up.

Mixing – Cartridges: Place cartridge in proper dispenser. To begin using a new cartridge, remove cartridge cap and dispense a small amount of adhesive, making sure Part A and Part B are extruding. Attach nozzle and dispense approximately 1-2" before applying onto the part being bonded. Partially used cartridges can be stored with mixing nozzle attached. To reuse, remove and discard the old nozzle, attach new nozzle and begin dispensing.

Application: Bonding surfaces should be clean and dry. For optimum surface preparation, consult Dexter's bulletin "Preparing the Surface for Adhesive Bonding". Once the adhesive is applied, the boned parts should beheld in contact until the part has developed handling strength. It is not necessary to clamp the parts unless movement during curing is likely.

Cure: Hysol 9460F is formulated for fast cure and handling time. Parts can be handled in 3-4 hours at room temperature Ultimate properties are achieved in 3 days at room temperature. Hysol 9460F can also be cured for 2 hours @ 140°F or  1 hour @ 180°F

Clean-up: It is important to remove excess adhesive from the work area and application equipment before it hardens. Many common solvents and citrus cleaners are suitable for removing uncured adhesive. Consult with your supplier's information pertaining to the safe and proper use of solvents.

Performance
Tensile Lap Shear Strength: (tested per ASTM D1002)
Cure                                                                             Test Temperature oF                                Typical Results
6 hours @ RT                                                             77                                                               2000 psi
18 hours @ RT                                                           77                                                               3500 psi
3 days @ RT                                                                77                                                              4000 psi
                                                                                     180                                                             400 psi

Floating Roller Peel Strength: (tested on etched aluminum per ASTM D3167)
3 days @ 77°F                                                             40 pli

Bulk Properties
Hardness (shore D) @ 77°F                                      80 minimum

Packaging
50 ml and 200 ml EPS Cartridges                              One and Five Gallon Systems