Hysol ® H4000  Email
 You may print this page for your file
Methacrylate Adhesive
Description
Dexter Hysol H4000 is a non-sagging, two component, room temperature curing, 10:1 mix ratio, methacrylate adhesive system. H4000 is formulated to reach fixture time rapidly. This adhesive forms resilient bonds and maintains its strength over a wide range of temperatures. H4000 is suitable for bonding a variety of substrates with a minimum of surface preparation for the most demanding bonding applications.
Recommended Substrates: PVC, polycarbonate, acrylic, ABS, stainless steel, epoxy coated metal and FRP
Features
Non-sagging gaps filled to 1/2 inch                         Superior impact and peel strength
Little or no surface preparation                                 Offers excellent tolerance to off-ratio mixing
Rapid room temperature cure100% reactive            Excellent environmental resistance

Typical Cured Properties
Tensile Strength (psi)                                       2,700 – 2,900                                ASTM D 638
Tensile Elongation (%)                                   30 – 40                                          ASTM D 638
Peel Strength (pli)                                            45                                                   ASTM D 3167
Tensile Lap Shear @ 77o F (psi)                     3,700 – 4,000                                ASTM D 1002
Tensile Lap Shear @ 180 o F (psi)                  1,900 – 2,100                                ASTM D 1002
Shore D Hardness                                           75 – 80
Bondline Thickness (inches)                          .005 – 0.50

Typical Uncured Properties
                                                Part A                             Part B                                               Mixed
Open Time @ 77°F                -                                       -                                                         7 - 10 minutes
Fixture Time @ 77°F              -                                       -                                                        15 – 20 minutes
Color                                       Cream                              Pale Yellow                                       Pale Yellow
Viscosity, cps                          90,000 – 100,000            160,000 – 170,000                             -
Brookfield HBT                     Spdl 6 @ 10rpm            Spdl 6 @ 10rpm                               -
Specific Gravity                       1.02                                 1.06                                                    1.02
Pounds/gallon                       8.50                                 8.84                                                    8.53
Mix Ratio
      by weight                          9                                     .61                                                       -
      by volume                        10                                    1                                                         -
 
Performance
 
Handling and Application

Mixing: It is highly recommended that either meter mix equipment or cartridges with static mix nozzles be used
to properly ratio and dispense the adhesive.  For hand mixing, combine Part A and Part B in the correct ratio
and mix thoroughly.  Once mixed, H4000 should achieve a uniform color.  This is important!  Heat buildup
during and after mixing is normal.  To reduce the likelihood of exothermic reaction or excessive heat buildup,
mix  less than 100 grams at a time.  Mixing smaller amounts will minimize heat buildup.

Applying: Bonding surfaces should be clean, dry, and free of contamination.  Extensive surface preparation is not
required for H4000, and good bonds can be formed on most substrates after a solvent wipe.  To assure maximum
bond strength, surfaces must be mated within the adhesive's open time.  Use enough material to completely fill
the joint when parts are clamped.
Curing:Parts should remain undisturbed during the interval of time between the material's open time and
fixture time.  After the fixture time is achieved the material has reached handling strength.  Temperature below
55°F will slow the cure; above 85°F will accelerate cure rate.
Clean Up: It is important to clean up excess adhesive from the work area and application equipment before it
cures.  Denatured alcohol and many common industrial solvents are suitable for removing uncured adhesive.  
Hysol H4000 is flammable.  Keep containers tightly closed after use.  Keep away from heat, sparks, and open
flames.
Storage
Hysol adhesives should be stored in a cool, dry place when not used for a long period of time. The shelf life for H4000 is one year from date of manufacture when stored at 40oF and six months when stored at room temperature or 77oF. Exposure above room temperature will reduce shelf life.
Packaging
100 gram clip packs 490ml EPS cartridges 5 Gallon 55 Gallon Drums

_______________________________________________________________________________________________________________
DISCLAIMER: The information supplied in this document is for guidance only and should not be construed as a warranty. All implied warranties are expressly disclaimed. Including without limitation any warranty of merchantability and fitness for use: All users of the materials are responsible for assuring that it is suitable for their needs, environment and use. All data is subject to change as Dexter deems appropriate.
Users should review the Material Safety Data Sheet (MSDS) and product label for the material to determine possible health hazards, appropriate engineering controls and precautions to be observed in using the material. Copies of the MSDS and label are available upon request.